Synthesis and Characterization of CrB2 by High Temperature and High Pressure Method
-
摘要: 采用高温高压手段,以单质硼粉和铬粉为原料,在压力为6 GPa、温度为1 200 ℃的条件下成功制备出CrB2化合物。利用X射线衍射仪、X射线能谱仪、硬度检测仪和扫描电子显微镜,对合成产物进行了物性表征。结果表明:合成的CrB2固体为六方结构,空间群为P6/mmm,晶格常数a=0.297 nm,b=0.307 nm;合成样品的晶粒直径为5~40 μm,结晶质量良好。硬度测试结果显示,高温高压合成的CrB2具有很高的硬度。对比实验条件和实验结果发现,温度和原料配比均影响CrB2的合成,提高原料中硼的比例有助于目标产物CrB2的形成。Abstract: With the elemental boron powder and chromium powder as raw materials, CrB2 compound was prepared successfully at 6 GPa and 1 200 ℃ by using high temperature and high pressure method.X-ray diffraction (XRD), X-ray energy dispersive spectroscopy (EDS), hardness tester and scanning electron microscopy (SEM) were used to characterize the physical properties of the sample.The results show that the synthetic CrB2 is hexagonal structure with space group of P6/mmm, and the lattice constants a and b are 0.297 and 0.307 nm, respectively.From the SEM micrographs, it can be seen that the grain diameter ranges from 5 to 40 μm, and the crystalline quality is good.Moreover, the synthetic sample exhibits high hardness value.By comparing the experimental results obtained under different synthetic conditions, it is found that both the temperature and ratio of raw materials affect the synthesis of CrB2, and an increase in the proportion of boron in raw materials contributes to the formation of the desired product CrB2.
-
Key words:
- high temperature and high pressure /
- CrB2 /
- X-ray diffraction /
- hardness
-
-
[1] 宿太超, 王琰弟, 马红安, 等.热电材料AgSbTe2的高温高压合成[J].超硬材料工程, 2008, 20(1): 455-499. http://en.cnki.com.cn/Article_en/CJFDTOTAL-ZBKJ200801014.htmSu T C, Wang Y D, Ma H A, et al. Synthesis of AgSbTe2 by high-pressure and high-temperature approach[J]. Superhard Material Engineering, 2008, 20(1): 455-499. (in Chinese) http://en.cnki.com.cn/Article_en/CJFDTOTAL-ZBKJ200801014.htm [2] 李翔, 刘清青, 冯少敏, 等.六八型大腔体二级推进高压高温装置与新材料的高压合成[J].高压物理学报, 2013, 27(2): 223-229. http://qikan.cqvip.com/Qikan/Article/Detail?id=46448978Li X, Liu Q Q, Feng S M, et al. The six over eight type double stage large volume high pressure and high temperature facilities and their applications to new materials syntheses[J]. Chinese Journal of High Pressure Physcis, 2013, 27(2): 223-229. (in Chinese) http://qikan.cqvip.com/Qikan/Article/Detail?id=46448978 [3] Qin L, Zhang X T, Yao L, et al. Preparation and characterization of nanocrystalline chromium boride[J]. J Mater Sci, 2006, 41(22): 7617-7619. doi: 10.1007/s10853-006-0853-6 [4] Kumar B M, Kumar S, Ganguli A K. Surface decoration through electrostatic interaction leading to enhanced reactivity: Low temperature synthesis of nanostructured chromium borides(CrB and CrB2)[J]. J Solid State Chem, 2013, 200: 117-122. doi: 10.1016/j.jssc.2013.01.005 [5] 孙天康, 汪成刚, 卢一鸣.自蔓燃高温合成CrB2[J].粉末冶金技术, 1998, 16(4): 256-257. http://www.cqvip.com/QK/95986X/19984/3257575.htmlSun T K, Wang C G, Lu Y M. Self-propagating high-temperature synthesis of chromium diboride[J]. Powder Metallurgy Technology, 1998, 16(4): 256-257. (in Chinese) http://www.cqvip.com/QK/95986X/19984/3257575.html [6] Jayaraman S, Klein E J, Yang Y, et al. Chromium diboride thin films by low temperature chemical vapor deposition[J]. J Vac Sci Technol A, 2005, 23(4): 631-633. doi: 10.1116/1.1927534 [7] 于润泽.几种量子功能材料的高压研制和物性研究[D].北京: 中国科学院研究生院, 2012: 35-36.Yu R Z. High-pressure research and physical research of several quantum functional materials[D]. Beijing: Graduate School of Chinese Academy of Sciences, 2012: 35-36. (in Chinese) [8] 赵旭东, 林峰, 刘晓旸, 等.富硼稀土硼化物NdB6的高温高压合成[J].高压物理学报, 1996, 10(3): 170-175. http://www.cqvip.com/Main/Detail.aspx?id=2146411Zhao X D, Lin F, Liu X Y, et al. Synthesis of boron-rich boride NdB6 under high pressure and high temperature[J]. Chinese Journal of High Pressure Physcis, 1996, 10(3): 170-175. (in Chinese) http://www.cqvip.com/Main/Detail.aspx?id=2146411 [9] Badzian A R. Superhard material comparable in hardness to diamond[J]. Appl Phys Lett, 1988, 53(25): 2495-2497. doi: 10.1063/1.100528 [10] 陈金兰, 秦家千, 王江华, 等.硼基超硬材料的研究进展[J].工具技术, 2010, 44(4): 7-8. http://www.cnki.com.cn/Article/CJFDTotal-GJJS201004003.htmChen J L, Qin J Q, Wang J H, et al. Research progress for superhard materials of boron-based system[J]. Tool Engineering, 2010, 44(4): 7-8. (in Chinese) http://www.cnki.com.cn/Article/CJFDTotal-GJJS201004003.htm [11] 李丹, 刘进, 胡娟, 等.聚晶立方氮化硼材料的性能及其应用[J].工具技术, 2006, 40(12): 11-14. http://www.cqvip.com/Main/Detail.aspx?id=23459379Li D, Liu J, Hu J, et al. Performance and application of polycrystalline cubic boron nitride[J]. Tool Engineering, 2006, 40(12): 11-14. (in Chinese) http://www.cqvip.com/Main/Detail.aspx?id=23459379