Effects of High Pressure Heat Treatment on the Thermal Physical Properties of Aluminum Bronze
-
摘要: 在5 GPa压力下对铝青铜进行750 ℃、保温15 min的高压热处理,对高压热处理前后铝青铜的电导率以及25~600 ℃温度范围内的热扩散系数、热容和热导率进行测试,结合显微组织的观察结果,探讨了高压热处理对铝青铜热物理性能的影响。研究表明:高压热处理能增大铝青铜的热扩散系数,减小热容;对热导率而言,温度低于400 ℃时高压热处理能增大铝青铜的热导率,而温度高于400 ℃时高压热处理能减小铝青铜的热导率。分析认为,产生变化的主要原因是高压热处理使铝青铜的微观组织发生了变化。Abstract: Aluminum bronze was treated at 5 GPa and 750 ℃ for 15 min, after that its electric conductivity, thermal diffusion coefficient, heat capacity, and thermal conductivity between 25 and 600 ℃ were measured. Combining these data with the microstructure images, the effects of high pressure heat treatment on the thermal physical properties of aluminum bronze were investigated. The results showed that high pressure heat treatment can increase the thermal diffusion coefficient and decrease the heat capacity of aluminum bronze. Furthermore, the thermal conductivity of aluminum bronze after high pressure heat treatment increases with increasing temperature until 400 ℃, and then starts to decrease. Analysis shows that this is because the high pressure heat treatment makes the microstructures of aluminum bronze alloy change.
-
Li W S, Wang Z P, Lu Y, et al. Preparation, Mechanical Properties and Wear Behaviors of Novel Aluminum Bronze for Dies [J]. Transactions of Nonferrous Metals Society of China, 2006, 16(3): 607-612. Straumal B B, Baretzky B, Mazilkin A A, et al. Formation of Nanograined Structure and Decomposition of Supersaturated Solid Solution during High Pressure Torsion of Al-Zn and Al-Mg Alloys [J]. Acta Mater, 2004, 52(15): 4469-4478. Wang Z L, Wang H W, Wei Z J, et al. High Pressure Solidification Microstructure and Stability of Al-9. 6%Mg Alloy [J]. The Chinese Journal of Nonferrous Metals, 2007, 17(3): 384-389. (in Chinese) 王振玲, 王宏伟, 魏尊杰, 等. Al-9. 6%Mg合金高压凝固组织及稳定性 [J]. 中国有色金属学报, 2007, 17(3): 384-389. Xu R, Zhao H, Li J, et al. Microstructures of the Eutectic and Hypereutectic Al-Ge Alloys Solidified under Different Pressures [J]. Mater Lett, 2006, 60(6): 783-785. Zhao J, Liu L, Yang J R, et al. Effects of High Pressure on the Microstructure and Hardness of a Cu-Zn Alloy [J]. Rare Metals, 2008, 27(5): 541-544. Wang H Y, Chen Y, Liu Y W, et al. Pressure Effects on Solid State Phase Transformation of Aluminium Bronze in Cooling Process [J]. Chinese Physics Letters, 2009, 26(10): 106201. Yang J R, Liu L, Ren Y J, et al. Effect of High Pressure and Heat Treatment on Microstructure of Aluminum Bronze [J]. Chinese Journal of High Pressure Physics, 2008, 22(3): 318-322. (in Chinese) 杨景茹, 刘琳, 任艳军, 等. 高压和热处理对铝青铜微观组织的影响 [J]. 高压物理学报, 2008, 22(3): 318-322. Tian R Z, Wang Z T. Cu Alloys and It's Working Handbook [Z]. Changsha: Central South University Press, 2002: 5. (in Chinese) 田荣璋, 王祝堂. 铜合金及其加工手册 [Z]. 长沙: 中南大学出版社, 2002: 5. Liu Y G, Xu L, Wang Q F, et al. Bulk -Fe/Nd2Fe14B Nanocomposite Magnets Prepared by the Phase Transition of Amorphous Nd9Fe81Co3Nb1B6 under High Pressure [J]. Mater Lett, 2008, 62(23): 3890-3892. Li H, Xu Y D, Zhang L T, et al. Thermophysical Properties of 2. 5D C/SiC Composites [J]. Journal of Aeronautical Materials, 2007, 27(4): 60-64. (in Chinese) 李宏, 徐永东, 张立同, 等. 2. 5D C/SiC复合材料的热物理性能 [J]. 航空材料学报, 2007, 27(4): 60-64. Wang F, Cai H, Wang Y P. The Microstructure and Properties of Fine Crystalline Al-50Si Alloy Prepared by High-Energy Ball Milling [J]. Chinese Journal of Materials Research, 2009, 23(5): 495-499. (in Chinese) 王菲, 蔡辉, 王亚平. 用高能球磨法制备的细晶Al-50Si合金的组织与性能 [J]. 材料研究学报, 2009, 23(5): 495-499. Dong Y H, Zhou X L, Hua X Z. Effect of Porosity on Thermal Performance of Mo-Cu Composite [J]. Hot Working Technology, 2008, 37(16): 1-4. (in Chinese) 董应虎, 周贤良, 华小珍. 孔隙率对Mo/Cu复合材料热物理性能的影响 [J]. 热加工工艺, 2008, 37(16): 1-4.
点击查看大图
计量
- 文章访问数: 7982
- HTML全文浏览量: 358
- PDF下载量: 817