摘要: 研究了非晶合金Fe73.5Cu1Nb3Si13.5B9(FINEMET)的激波晶化。与退火晶化比较,激波晶化具有一系列鲜明特征,这些特征是固态下扩散性相变理论难以解释的,有深刻的物理内涵。Abstract: Shock-wave and annealing crystallizations of alloy FINEMET were studied using XRD, DSC and TEM. It was found that amorphous FINEMET samples transformed into nanocrystals with grain size of 30~50 nm under shock loading. Comparing with annealing crystallization, many characteristics in the shock wave crystallization can not be explained using diffusion theory. The shock wave nanocrystallization of amorphous alloy contains plentiful physical connotation.
-
Yoshizawa Y, Oguma S, Yamauchi K. New Fe-Based Soft Magnetic Alloys Composed of Ultrafine Grain Structure [J]. Appl Phys, 1998, 64: 6044. Koster U, Schunemann U, Black-Bewerdorff M. Nanocrystalline Materials by Crystallization of Metal-Metaloid Glasses [J]. Mat Sci Eng, 1991, A133: 661. Heczko O, Ruuskanen P. Magnetic Properties of Compacted Alloy Fe73.5Cu1Nb3Si13.5B9 in Amorphous and Nanocrystalline State [J]. IEEE Trans on Magn, 1994, 29: 2670. Ruuskanen P. Magnetic Properties of Fe73.5Cu1Nb3Si13.5B9 Alloy Compacted by a Shock-Wave Technique [J]. J Mag Mat, 1998, 182: 185. 刘佐权, 赵鹤云, 吕毓松, 等. 激波诱导非晶合金Fe78B13Si9的晶化 [J]. 金属学报, 1996, 32(8): 862. 张延中, 樊岳良. Fe73.5Cu1Nb0.5Mo2.5Si12B10超微晶合金的磁性及应用 [J]. 金属材料研究, 1992, 18: 50. 刘应开, 候德东, 周效锋, 等. 非晶(Fe0.99Mo0.01)78Si9B13, Fe78Si9B13合金激波晶化主相-Fe变化研究 [J]. 物理学报, 1999, 48(12): 2304. 刘应开, 周效锋, 刘佐权, 等. 非晶合金的激波晶化实验研究 [J]. 髙压物理学报, 1999, 13(3): 230. 周效锋, 刘应开, 刘佐权, 等. Fe73.5Cu1Nb3Si13.5B9非晶态合金的激波纳米晶化研究 [J]. 物理学报, 1999, 48(11): 2098. 刘佐权, 张远第, 刘贤, 等. FINEMET非晶合金激波晶化中Cu和Nb作用的失效 [J]. 金属学报, 2000, 36(2): 120.
点击查看大图
计量
- 文章访问数: 8348
- HTML全文浏览量: 568
- PDF下载量: 704