The Formation of a New Approximant of Decagonal Quasi-Crystal in Al6FeYb Alloy under High Static Pressure
-
摘要: 对掺稀土钇的铝铁合金(Al6FeYb)进行了静高压(4.8 GPa)熔态(1 400 ℃)淬火(冷却速率100 ℃/s)研究。使用透射电镜对样品中形成的微结构进行了观察。首次在该系统中发现了一个十次准晶相关晶体相。实验分析表明,该相为底心正交晶体相,电镜测得的晶胞参数为a=0.716 nm,c=2.195 nm。用已有的理论对该相的结构形成进行了讨论。Abstract: In the investigations, samples of Al6FeYb alloy were quenched with a cooling rate of 102 K/s from melting state (1 400 ℃) under high static pressure (4.8 GPa). A new crystalline approximant was observed and its structure was a B-type orthorhombic crystalline phase with the lattice parameters of a=0.716 nm, c=2.195 nm. The structure and formation of the crystalline approximant were discussed by the current theory.
-
Key words:
- cystalline approximant /
- high-static pressure /
- quench from melting state /
- Al6FeYb
-
Fitzgerald J D, Withers R L, Steuart A M, et al. Phil Mag B, 1988, 58: 55. Edagawa K, Suzuki K, Ichihara M, et al. Phil Mag B, 1991, 64: 629. Horn P M, Menzfeldt W, Divincenzo D P, et al. Phys Rev Lett, 1986, 57: 1444. Yu R C, Li X Z, Yu D P, et al. Phil Mag Lett, 1993, 67(4): 287. 许大鹏, 宿新堂, 禹日成, 等. 高压物理学报, 1993, 7(2): 132. Ma L, Wang R, Kuo K H. Scr Metall, 1988, 22: 1791. Lubensky T C, Socolor J E, Steinhardt P J, et al. Phys Rev Lett, 1986, 57: 1440. Zhang H, Kuo K H. Phys Rev, 1990, 42(14): 8907.
点击查看大图
计量
- 文章访问数: 7073
- HTML全文浏览量: 346
- PDF下载量: 665