- Phase Transition under Pressure, Constant Magnetic Permeability and Its Pressure as Well as Frequency Characteristic in Nanometer-Scale Powder of Invar Alloy
-
摘要: 以Fe-30wt%Ni合金片为母合金,用蒸发冷凝法制备了三种粗细不同的纳米微粒。经透射电镜和X光衍射物相分析,微粒成分与母合金一致。5T、5H和3K粉的平均粒度分别为13.6、27和40 mm。在室温和43~28个不同的流体静压力(0.000 1~2.205 GPa)下测量了它们的磁化曲线、磁导率曲线和起始磁化曲线。结果表明:(1)在H=(20-132)(1000/4)A/m范围内Fe-30Ni合金三种纳米粉均具有恒磁导率。(2)三种纳米粉恒磁导率随静水压的变化规律如下:r=3.83+0.253p-0.022 1p2-0.007 22p3(5T粉);r=3.93+1.20p-1.97p2+1.52p3-0.510p4+0.059 9p5(5H粉);r=5.96-0.276p+0.107p2-0.045 9p3(3K粉)。前两者随压力增加而升高。后者随压力增加而下降。(3)-马氏体相变明显存在于5T、5H粉中,而3K粉中未见到。(4)Fe-30Ni合金片的i从200kHz至2 MHz已下降一个数量级,而其纳米粉i的频率范围高于300 MHz,增大两个数量级以上。Abstract: By means of evaporation and condensation, three kinds of nanometer-scale powder of invar alloy (Fe-30wt%Ni) were prepared. It is found out with the method of TEM and X-ray diffraction that their composition coincides with its matrix alloy, average grain size is 13.6 nm (powder 5T) and 27 nm (powder 5H) and 40 nm (powder 3K). Under room temperature and hydrostatic pressure of 43~28 different magnitudes ranging from 0.000 1 to 2.205 GPa, the magnetization curve and initial magnetization curve were measured to see their relation with pressure. The authors point out: (1) the three kinds of nanometer-scale powder of invar alloy (Fe-30wt%Ni) all possess constant magnetic permeability when H=(20-132)(1000/4)A/m; (2) constant magnetic permeability, r varies with the pressure as follows: r=3.83+0.253p-0.022 1p2-0.007 22p3, r=3.93+1.20p-1.97p2+1.52p3-0.510p4+0.059 9p5, r=5.96-0.276p+0.107p2-0.045 9p3 , r of powder 5T and 5H rises, but r of powder 3K decreases when pressure increases; (3) - Martensite phase transition under high pressure exists obviously in ultramicron 5H and 5T, but not in ultramicron 3K; (4) i of Fe-30wt%Ni alloy piece decreases in one order of magnitude in the frequency range from 200 kHz to 2 MHz, but when frequency range for their ultramicrons is over 30 MHz, the value of i does not decrease greatly so its frequency range extents two orders of magnitude as compared with its piece.
-
Guillaume C E. Compt Rend, 1897, 125: 235. 近角聪信, 等. 杨膺善, 韩俊德译. 磁性体手册(中册). 北京: 冶金工业出版社, 1985: 11, 108, 114. Grangle J, Hallam G C. Proc Phys Soc A, 1963, 272: 119. Kondorsky E I, Sedov V L. Sov Phys JETP, 1959, 35: 586. Kondorsky E I, Sedov V L. J Appl Phys, 1960, 31: 3315. Gupta K P, Cheng C H, Beck P A. J Phys Chem Solids, 1964, 25: 73. Burford J C, Graham G M. Can J Phys, 1965, 43: 1915. Hausch G, Warlimont H. Z Metalk, 1972, 63: 547. Fletcher R. J Phys C, 1969, 2: 2107. 苏昉, 车荣钲, 许伟, 等. 高压物理学报, 1990, 4: 63-71. 苏昉, 苏骏, 许伟. 高压物理学报, 1993, 7: 11-21. 王建波, 许应凡, 麦振洪, 等. 日本理学X射线衍射用户协会论文选集, 天津: 天津新华印刷厂, 1994, 7(1): 40. 王文鼎, 都有为, 臧文成. 全国第二届纳米固体学术讨论会论文集, 合肥, 1991. 陆怀先, 刘荣川, 王连卫, 等. 全国第二届纳米固体学术讨论会论文集, 合肥, 1991. 李华, 赵中仁. 全国第二届纳米固体学术讨论会论文集, 合肥, 1991. 钟文定. 铁磁学(中册). 北京: 科学出版社, 1992. 陆怀先, 王锦辉. 第八届全国磁学磁性材料会议论文集, 山东烟台, 1993. Bolling G F, Arrott A, Richman R H. Phys Stat Sol, 1968: 26-743. Asano H. J Phys Soc Jpn, 1969, 27: 542; 1968, 25: 286. Bando Y. J Phys Soc Jpn, 1964: 19-237. Nakamura Y, Shiga M, Shikazono N. J Phys Soc Jpn, 1964, 19: 1177. Rhiger D R, Ingalls R. Phys Rev Lett, 1972, 28: 749. Donaldson R H. Phys Rev, 1967, 157: 368. Callen E, Cailen H B. Phys Rev A, 1965, 139: 455. Weiss R J. Proc Phys Soc, 1963, 82: 281. 苏昉, 谢斌, 陈允鸿. 高压物理学报, 1996, 9: 247.
点击查看大图
计量
- 文章访问数: 7046
- HTML全文浏览量: 456
- PDF下载量: 665