A Study on New Orthorhombic Approximants of the Al70Co15Tb5Ni10 Decagonal Quasi-crystal
-
摘要: 使用静高压熔态淬火方法,在Al70Co15Tb5Ni10合金中截获到迄今为止晶胞参数最大的两个十次准晶的Penrose-Tiling相关相。其晶胞参数分别为:简单正交晶体a=6.11 nm,b=0.4 nm,c=8.4 nm;底心正交晶体a=6.11 nm,b=0.4 nm,c=8.4 nm。其晶体结构和晶胞参数与目前理论上的预言基本吻合。
-
关键词:
- 准晶相关相 /
- AlCoTbNi合金 /
- 静高压 /
- 熔态淬火
Abstract: Two new orthorhombic approximants with the largest until cell observed up to now were found in the Al70Co15Tb5Ni10 decagonal quasi-crystal, which were prepared by quenching (102 ℃/s) the melt state (1 700 ℃) under high static pressure (7.0 GPa). The lattice parameters of the orthorhombic approximant are the same (a=6.1 nm, b=0.4 nm, c=8.4 nm), but the structure of the first phase is P-type and that of the second phase is a B-type. Their structures and lattice parameters are in accordance with that of the present theoretical predictions. -
Entin-wohlman G, Kleman M, Pavlovitch. J Phys (Fr), 1988, 49: 587. Mosseri R, Oguey C, Duneau M. In: Quasicrystalline Materials, edited by Ch Janot and J M Dubois. Sin Gapore: World Scientific, 1988: 224. Zhang H, Kuo K H. Phys Rev B, 1990, 42(14): 8907. 苏文辉, 许大鹏, 刘宏建, 等. 吉林大学自然科学学报, 1992, 特刊: 170-187. 楚树成, 许大鹏, 苏文辉. 高压物理学报, 1990, 4(2): 137. Bendersky L. Phys Rev Lett, 1985, 55(14): 1461. Ishihara K N. Mater Sci Forum, 1987, 22-24: 223.
点击查看大图
计量
- 文章访问数: 7392
- HTML全文浏览量: 442
- PDF下载量: 615