摘要: 本文通过扫描电子显微镜等实验手段,研究了Bi系超导材料在不同制备条件下的显微结构,着重分析了压力下(冷压、热压)样品显微结构的变化。经过压力处理,超导晶粒的平均尺寸显著降低,气孔率大幅度减少,样品密度得以极大提高,达理论密度的90%~95%。在经冷压、热压处理的样品中可见到明显的晶粒择优取向排列,其形成机制是压力下的塑性流变以及晶粒的各向异性生长趋势。
-
关键词:
- BiPbSrCaCuO超导体 /
- 冷压 /
- 热压 /
- 显微结构
Abstract: Microstructures of BiPbSrCaCuO superconductors prepared under various conditions were investigated by means of the scanning electronic microscope (SEM). Focus was placed on the microstructure change of the samples treated by cold pressure and hot pressing. Due to the effects of pressure, average grain sizes in the pressed samples decreased remarkably, and the bulk densities increased greatly to reach 90%~95% of the theoretic density. The high pressure treated samples, on the other hand, are found to be obvious oriented, which may result from the plastic flow under high pressure and the anisotropic growing of the superconducting grains.-
Key words:
- BiPbSrCaCuO superconductor /
- cold pressing /
- hot pressing /
- microstructure
-
Maeda H, et al. Jpn J Appl Phys, 1988, 27: L209. Kijima N, et al. Jpn J Appl Phys, 1988, 27: L821. Muromachi E T, et al. Jpn J Appl Phys, 1988, 27: L556. Cava R J, Batlogg B, Sunshine S A, et aI. Physica C, 1988, 153-155: 560. Endo U, Koyama S, Kawai T. Jpn J Appl Phys, 1988, 27: L1476. Zhang J Z, McCartney D G, Humphreys C J. Supercond Sci Technol, 1990, 3: 185. Takeda Y, et al. Physica C, 1989, 159: 789. Kikuchi A, et al. Jpn J Appl Phys, 1988, 27: L2300. 姚玉书, 黄新明, 吴冰薄, 等. 物理学报. 吴冰青, 姚玉书, 靳常青, 等. 低温物理学报, 1991, 13. Aslan M, et al. J Am Ceram Soc, 1990, 73: 150. Singh B P, et al. Jpn J Appl Phys, 1988, 27: L1116. Asano T, et al. Jpn J Appl Phys, 1988, 27: L1652.
点击查看大图
计量
- 文章访问数: 8015
- HTML全文浏览量: 1869
- PDF下载量: 652