Fragmentation of Metal Cylindrical Shell Treated by Local Quenching
-
摘要: 采用局部淬火技术对40Cr钢柱壳进行预制处理,考察了淬硬区和基体的组织特征,并对柱壳的破碎性能进行了研究。结果表明:预制后淬硬区组织主要为针状和板条状马氏体,晶粒细化,并且脆性变大。基于此性能差异,柱壳在内部载荷作用下按设计方式破碎,破片质量分布均匀,穿透性符合要求。研究结果可为弹体设计提供一定的参考。Abstract: The fragmentation and penetration of the 40Cr steel cylindrical shells preformed by local quenching technology were studied experimentally.Through scanning electron microscopy (SEM) analysis, it is found that the microstructure of hardened layer in the cylindrical shell is predominantly needle and lath type martensite, and it is more refined and brittle than bulk material.Based on the performance difference, the steel cylindrical shell fractures along the designed path during the expansion process.The mass distribution of the preformed fragments is relatively uniform and the penetration also meets the requirement, which can provide reference for design of ammunition.
-
Key words:
- cylindrical shell /
- preformed fragments /
- quenching /
- fragmentation /
- penetration
-
表 1 40Cr钢的化学成分(质量分数)
Table 1. Chemical composition of 40Cr steel (Mass fraction)
(%) C Si Mn Cr P S 0.39 0.25 0.60 0.88 ≤0.035 ≤0.035 表 2 热处理工艺参数
Table 2. Heat treatment parameters
Process Treatment temperature/(℃) Treatment time/(h) Cooling method Normalizing 880 1.5 Air cooling Quenching 860 1.0 Oil cooling Tempering 650 1.5 Water cooling 表 3 穿透性测试结果
Table 3. Results of penetration tests
Exp.group No. Ntot Np ap/(%) d=4 m d=6 m d=8 m d=4 m d=6 m d=8 m d=4 m d=6 m d=8 m Shell
upwards1 12 18 24 12 10 6 100.0 55.6 25.0 2 12 18 24 8 13 9 66.7 72.2 37.5 3 12 18 24 10 9 10 83 50.0 41.7 4 12 18 24 10 10 8 83.3 55.6 33.3 5 12 18 24 10 11 9 83.3 61.1 37.5 Shell
downwards1 12 18 24 11 12 10 91.7 66.7 41.7 2 12 18 24 10 12 11 83.3 66.7 45.8 3 12 18 24 12 13 10 100.0 72.2 41.7 4 12 18 24 10 13 9 83.3 72.2 37.5 5 12 18 24 11 11 11 91.7 61.1 45.8 -
[1] 郑慕侨, 冯崇植, 蓝祖佑.坦克装甲车辆[M].北京: 北京理工大学出版社, 2003.Zheng M Q, Feng C Z, Lan Z Y. Tank and Armoured Vehicle[M]. Beijing: Beijing Institute of Technology Press, 2003. (in Chinese) [2] 付源辉, 陶钢, 李守渤, 等.小口径榴弹定向杀伤技术的威力和分布均匀性[J].弹道学报, 2005, 17(4): 50-54. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=ddxb200504011Fu Y H, Tao G, Li S B, et al. Fragments ahead flighting lethality and distribution homogeneity for small caliber grenade[J]. Journal of Ballistics, 2005, 17(4): 50-54. (in Chinese) http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=ddxb200504011 [3] 安纯前, 李阿楠, 王东为.杀伤榴弹威力结构的设计与研究[J].弹箭与制导学报, 2003, 23(增2): 151-153. http://www.cnki.com.cn/Article/CJFDTotal-DJZD2003S2023.htmAn C Q, Li A N, Wang D W. Technical analysis and proof of power structure of battle-part of shrapnel[J]. Journal of Projectiles, Rockets, Missiles and Guidance, 2003, 23(Suppl 2): 151-153. (in Chinese) http://www.cnki.com.cn/Article/CJFDTotal-DJZD2003S2023.htm [4] 赵捍东, 金丽, 翟玉兰, 等.预制破片杀伤威力影响因素分析[J].弹箭与制导学报, 2007, 27(2): 150-151. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=djyzdxb200702047Zhao H D, Jin L, Zhai Y L, et al. Analysis on the influencing factors of the lethality about premade fragments[J]. Journal of Projectiles, Rockets, Missiles and Guidance, 2007, 27(2): 150-151. (in Chinese) http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=djyzdxb200702047 [5] 陈炯, 袁书强, 周春华, 等.高能束控制破碎钨合金壳体破碎效果研究[J].兵器材料科学与工程, 2010, 33(6): 62-64. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=bqclkxygc201006019Chen J, Yuan S Q, Zhou C H, et al. Fragmentation effect of tungsten alloy shells controlled by high-energy-beam[J]. Ordnance Material Science and Engineering, 2010, 33(6): 62-64. (in Chinese) http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=bqclkxygc201006019 [6] 刘峰涛, 袁书强, 陈炯, 等.高能束控制破碎弹体威力对比研究[J].兵器材料科学与工程, 2008, 31(1): 67-70. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=bqclkxygc200801018Liu F T, Yuan S Q, Chen J, et al. Comparative study on the shell power after high-energy-beam controlled fragmentation[J]. Ordnance Material Science and Engineering, 2008, 31(1): 67-70. (in Chinese) http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=bqclkxygc200801018 [7] 机械电子工业部兵器标准化研究所. GJB 3197─1998炮弹试验方法[S].中国: 机械电子工业部兵器标准化研究所, 1998: 105-108.Weapons Machinery and Electronics Industry Standardization Institute. GJB 3197─1998 Test method for projectile[S]. China: Weapons Machinery and Electronics Industry Standardization Institute, 1998: 105-108. (in Chinese) [8] 隋树元, 王勋, 马晓青, 等.内爆炸载荷下弹钢的动态变形与断裂准则研究[J].兵工学报, 1996, 17(1): 88-92. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=QK199600175206 [9] Zecevic B, Catovic A, Terzic J. Comparison of lethal zone characteristics of several natural fragmenting warheads[J]. Cent Eur J Energ Mater, 2008, 5(2): 67-81. http://www.researchgate.net/publication/229050541_Comparison_of_Lethal_Zone_Characteristics_of_Several_Natural_Fragmenting_Warheads [10] 马永忠, 李其祥, 罗坤, 等.杀伤榴弹杀伤面积的计算及影响因素分析[J].弹箭与制导学报, 2005, 25(2): 346-348. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=djyzdxb200502113