低密度聚氨酯泡沫压缩行为实验研究

林玉亮; 卢芳云; 王晓燕; 赵习金

doi:10.11858/gywlxb.2006.01.017

低密度聚氨酯泡沫压缩行为实验研究

doi: 10.11858/gywlxb.2006.01.017

国防科技大学理学院技术物理研究所，湖南长沙 410073

详细信息

通讯作者:
林玉亮

计量
- 文章访问数: 7640
- HTML全文浏览量: 495
- PDF下载量: 958
出版历程
- 收稿日期: 2004-11-30
- 修回日期: 2005-01-27
- 发布日期: 2006-03-05

Experimental Study of the Compressible Behavior of Low-Density Polyurethane Foam

Department of Applied Physics, National University of Defense Technology, Changsha 410073, China

More Information

Corresponding author: LIN Yu-Liang

摘要

摘要: 在室温下，对一种低密度硬质聚氨酯泡沫进行了准静态压缩及应变率在1103～5103 s-1范围内的冲击压缩实验。结果表明，所测试的聚氨酯泡沫材料在准静态实验与动态实验之间存在明显的应变率效应，但在纯动态实验中应变率效应不明显。最后，给出了以屈服应力、密度、应变等为参量的动态压缩本构关系，且能较好地与材料的动态压缩曲线吻合。
- 分离式霍普金森压杆 /
- 本构关系 /
- 聚氨酯泡沫 /
- 高应变率
Abstract: The compressive stress-strain behaviors of polyurethane foams in four different mass densities have been tested by SHPB at strain rates of 1103～5103 s-1. Experimental results show that the compressive behavior of the polyurethane foam is sensitive to the strain rates between quasi-static experiments and SHPB experiments. However, the behavior is not sensitive to the strain-rate under condition of dynamic compression. A experiential constitutive relation, which considers density effect of the foams on materials features at high strain-rates, has been proposed based on Sherwood model. The relation is well agreed to the experimental data.
- Split Hopkinson Pressure Bar /
- constitutive relation /
- polyurethane foam /
- high strain rate

HTML全文

参考文献(13)

Goods S H, Neuschwanger C L, Henderson C C, et al. Mechanical Properties of CRETE, a Polyurethane Foam [J]. J Appl Poly Sci, 1998, 68: 1045-1055.

Jun Zh, Noboru K, Victor Li. Constitutive Modeling of Polymeric Foam Material Subjected to Dynamic Crush Loading [J]. Inter J Impact Eng, 1998, 21(5): 369-386.

Hu Sh Sh, Liu J F, Wang W. Study on the Constitutive Relationship of Rigid Polyurethane Foam [J]. Acta Mechanica Sinica, 1998, 30(2): 151-156. (in Chinese)

胡时胜, 刘剑飞, 王悟. 硬质聚氨酯泡沫塑料本构关系的研究 [J]. 力学学报, 1998, 30(2): 151-156.

Lu Z X, Zhu W M, Kou C H, et al. Investigation on the Fracture Properties of Polyurethane Rigid Foam Plastics [J]. Acta Mechanica Sinica, 2002, 32(5): 627-631. (in Chinese)

卢子兴, 朱汪鲲, 寇长河, 等. 聚氨酯泡沫塑料的强度与断裂韧性 [J]. 力学学报, 2002, 32(5): 627-631.

Lu Z X, Xie R Z, Tian C J. Investigation into Shear Mechanical Properties of PUR Foamed Plastics [J]. J Beijing Univer Aero Astro, 1999, 25(5): 561-564. (in Chinese)

卢子兴, 谢若泽, 田常津. 聚氨酯泡沫塑料剪切力学性能的研究 [J]. 北京航空航天大学学报, 1999, 25(5): 561-564

Chen W, Lu F, Zhou B. A Quartz-Crystal-Embedded Split Hopkinson Pressure Bar for Soft Materials [J]. Experimental Mechanics, 2000, 40(1): 1-56.

Nemat-Nasser S, Isaacs J B, Starrett J E. Hopkinson Techniques for Dynamic Recovery Experiments [J]. Proceedings of the Royal Society of London, 1991, 435(A): 371-391.

Frew D J, Forrestal M J, Chen W. Pulsing Shaping Techniques for Testing Brittle Materials with a Split Hopkinson Pressure Bar [J]. Experimental Mechanics, 2002, 42(1): 93-106.

Sherwood J A, Forst C C. Constitutive Modeling and Simulation of Energy Absorbing Polyurethane Foam [J]. Poly Eng Sci, 1992, 32(16): 1138-1146.

Chen W, Lu F, Winfree N. High-Strain-Rate Compression Behavior of a Rigid Polyurethane Foam with Various Densities [J]. Exp Mech, 2002, 42(1): 65-73.

施引文献

资源附件(0)

访问统计