铝阳极化冲击波探针的工艺探索

孙悦 袁长迎 张修路 吴国栋

孙悦, 袁长迎, 张修路, 吴国栋. 铝阳极化冲击波探针的工艺探索[J]. 高压物理学报, 2004, 18(2): 157-162 . doi: 10.11858/gywlxb.2004.02.011
引用本文: 孙悦, 袁长迎, 张修路, 吴国栋. 铝阳极化冲击波探针的工艺探索[J]. 高压物理学报, 2004, 18(2): 157-162 . doi: 10.11858/gywlxb.2004.02.011
SUN Yue, YUAN Chang-Ying, ZHANG Xiu-Lu, WU Guo-Dong. A Kind of Anodized Aluminium Shock Wave Detectors[J]. Chinese Journal of High Pressure Physics, 2004, 18(2): 157-162 . doi: 10.11858/gywlxb.2004.02.011
Citation: SUN Yue, YUAN Chang-Ying, ZHANG Xiu-Lu, WU Guo-Dong. A Kind of Anodized Aluminium Shock Wave Detectors[J]. Chinese Journal of High Pressure Physics, 2004, 18(2): 157-162 . doi: 10.11858/gywlxb.2004.02.011

铝阳极化冲击波探针的工艺探索

doi: 10.11858/gywlxb.2004.02.011
详细信息
    通讯作者:

    孙悦

A Kind of Anodized Aluminium Shock Wave Detectors

More Information
    Corresponding author: SUN Yue
  • 摘要: 为了在定形纯铝棒材(35 mm1.0 mm)上制取既薄、完整,又均匀、致密且电绝缘强度较高的绝缘膜,首先根据阳极化电解原理,测定了铝棒半球形端的极化曲线,获得了在50~60 ℃温度环境下铝绝缘膜稳定生长的区域在3~13 V之间这一重要的工艺条件;然后给出了铝电探针阳极化的步骤和相应的工艺参数。从而摸索出可批量生产适于液体冲击压缩实验的、性能一致性好、可靠性高的冲击波速度探测器的实验方法。同时,分析了电解系统温度条件以及沸水封孔工艺对强化铝绝缘膜的物理性质和电绝缘强度的影响。由此工艺可均匀地制得厚度在4~15 m之间的Al2O3薄膜,在给定温度下制得平均厚度为6 m的电探针耐直流电压为250 V、1 min,在液氮温度(77 K)下静置4 h后绝缘膜的物理外观和电绝缘强度都未发生变化。借助300 Nm冲击力发生器,测得该类探针的开关一致性不大于20 ns。在较高冲击压力下,该特性有望得到进一步改善。

     

  • Pan H B. A New Phase Transition of -Quarts GeO2 by Molecule Dynamics Simulation [J]. J Chem Phys, 2000, 13(6): 666-672. (in Chinese)
    潘海波. -Quarts GeO2高压相变的分子动力学研究 [J]. 化学物理学报, 2000, 13(6): 666-672.
    Cui Q L, Tu B Z, Liu J, et al. Synchrotron Diffraction of Gallium Oxide under High Pressure [J]. Chinese Journal of High Pressure Physics, 2002, 16(2): 81-84. (in Chinese)
    崔启良, 涂宝招, 刘景, 等. 氧化镓的同步辐射研究 [J]. 高压物理学报, 2002, 16(2): 81-84.
    Zhang X Y, Zhang J W, Wang W K, et al. The Form of the Nano-Crystallization Alloy of FeCuNbSiB under the High Pressure [J]. Science in China (Series A), 1998, 28(12): 1117. (in Chinese)
    张湘义, 张静武, 王文魁, 等. 高压下FeCuNbSiB纳米晶合金的形成 [J]. 中国科学 ( A辑 ), 1998, 28(12): 1117.
    Zhang X Y, Zhang J W, Wang W K. A Novel Route for the Preparation Nanocomposite Magnets [J]. Advanced Materials, 2000, 12(19): 1441.
    Xu Z Y. Progress and Perspective in Material Heat Treatment [J]. Transaction of Material Heat Treatment, 2003, 24(1): 1. (in Chinese)
    徐祖耀. 材料热处理的进展和瞻望 [J]. 材料热处理学报, 2003, 24(1): 1.
    Zhang J W, Zhang X Y, Pan Y, et al. TEM Analysis of Nanometer Multi-Layer Structure of Low Carbon Steel [A]. China-Russia Seminar on Nonegui Librium Phase Transitipn under Ultra Conditions NEPTUC [C]. Qinhuangdao: Yanshan University, 2001.
    Feng D, Wang Y N, Qiu D R. Metal Physics [M]. Beijing: Science Press, 1975: 3-4. (in Chinese)
    冯端, 王业宁, 丘第荣. 金属物理 [M]. 北京: 科学出版社, 1975: 3-4.
    Zhang B, Peng Y H, Lu X, et al. Study of Martensite Transformation of Alloys [J]. Acta Metallurgica Sinica, 2001, 37(12): 1238-1242. (in Chinese)
    张斌, 彭颖红, 陆兴, 等. Fe-24Mn-Ge合金马氏体相变的研究 [J]. 金属学报, 2001, 37(12): 1238-1242.
    Wang X X, Zhao L C. The Stabilization of Deformed Stress-Induced Martensite and Its Effect on Shape Memory Effect in an Fe-Mn-Si-Ni-Co Alloy [J]. Functional Material, 1994, 25(5): 440-445. (in Chinese)
    王小祥, 赵连城. Fe-Mn-Si-Ni-Co 合金中形变应力诱发马氏体的稳定化及其对记忆效应的影响 [J]. 功能材料, 1994, 25(5): 440-445.
  • 加载中
计量
  • 文章访问数:  14585
  • HTML全文浏览量:  682
  • PDF下载量:  1063
出版历程
  • 收稿日期:  2003-08-04
  • 修回日期:  2004-01-05
  • 发布日期:  2004-06-05

目录

    /

    返回文章
    返回