摘要: 通过回收破片的断口观察和金相分析研究了LY12铝圆管在高应变率压缩过程中的剪切断裂现象;回收破片具有典型的剪切断裂特征,断口与径向近似成45夹角,断口观察发现断口面经历过径向摩擦;破片金相分析表明,绝热剪切带和裂纹首先在圆管内壁附近产生,然后沿最大剪应力线向外壁扩展。利用数值计算给出了圆管在内爆压缩加载下管壁内微元的应力、应变历史,为分析LY12铝圆管的剪切断裂提供了参考。Abstract: In this paper, the shear fracture performances of LY12 aluminum cylinder were studied under explosive loading. The recovered fragments showed shear characteristics. The fracture surface formed along the maximum shear stress curves. SEM images of the recovered fragments illustrate that the fracture surfaces have undergone friction. The adiabatic shear bands and microcracks all initiate near the inside wall and develop along the maximum shear stress curves to the outside wall of the cylinder. The histories of stress and strain from numerical calculations indicate the adiabatic shear bands initiate more easily near the inside of cylinder than in other zones, which corresponds to the results of metallographic analysis.
-
Key words:
- LY12 aluminum cylinder /
- high-strain rate /
- shear fracture /
- adiabatic shear band
-
Taylor G I. Science Papers of Sir G. I. Taylor [M]. London: Cambridge University Press, 1963: 387. Slate P M B, Billings M J W, Fuller P J A. The Rupture Behavior of Metals at High Strain Rates [J]. J Inst Metals, 1967, 95: 244-251. Hoggatt C, Recht R. Fracture Behavior of Tubular Tombs [J]. J Appl Phys, 1968, 39: 1856-1862. Grady D E, Hightower M M. Fracture of a 4140 Steel Cylinder under High Explosive Loading [R]. Sand-90-0882C, 1990. Martineau R L. A Viscoplastic Model of Expansioning Cylindrical Shells Subjected to Internal Explosive Detonations [R]. LA-13424-T, 1998. Zhang K. The Experimental Study on the Flying Process of the Metal Cylinder with Outer Explosive Loading [A]. The Proceeding of Detonation Driving and Instable Growing-up of Detonation [C]. Kunming, China, 1985. (in Chinese) 张凯. 圆筒在外布炸药滑移爆轰载荷作用下飞行姿态和实验研究 [A]. 爆轰驱动和爆轰不定常增长会议论文集 [C]. 昆明, 1985. Feng J B. Deformation and Fracture of the Metal Cylinder with Internal Explosive Load [D]. Mianyang: Post-Graduate Department of CAEP, 1988. (in Chinese) 封加波. 爆炸载荷下金属柱壳的变形和破坏规律研究 [D]. 绵阳: 中国工程物理研究院研究生部, 1988. Nesterenko V F, Meyers M A, Wright T W. Collective Behavior of Shear Bands [A]. Murr L E, Staudhammer K P, Meyers M A. Metallurgical and Materials Applications of Shock-Wave and High-Strain-Rate Phenomena [C]. The Netherlands, 1995: 397-404. Meyers M A, Nesterenko V F. High-Strain-Rate Deformation of Tantalum: The Thick-Walled Cylinder Method [A]. Murr L E, Staudhammer K P, Meyers M A. Metallurgical and Materials Applications of Shock-Wave and High-Strain-Rate Phenomena [C]. The Netherlands, 1995: 487-494. Tang T G. Study on the Shear Fracture of Steel Cylinder under Imploding Load [J]. Chinese Journal of High Pressure Physics, 2002, 16(1): 75-79. (in Chinese) 汤铁钢. 内爆压缩加载下抗氢钢圆管剪切断裂研究 [J]. 高压物理学报, 2002, 16(1): 75-79. Tang T G. Studies on the Thermoplastic Instability and Shear Fracture of Metal Cylinder under Imploding Load [D]. Mianyang: Post-Graduate Department of CAEP, 2002. (in Chinese) 汤铁钢. 内爆加载下金属圆管的热塑剪切失稳与断裂研究 [D]. 绵阳: 中国工程物理研究院研究生部, 2002.
点击查看大图
计量
- 文章访问数: 7731
- HTML全文浏览量: 339
- PDF下载量: 815