掺杂立方氮化硼对金刚石聚晶致密化和显微结构的影响

周振君; 李工; 杨正方; 陈玉如

doi:10.11858/gywlxb.2001.03.011

掺杂立方氮化硼对金刚石聚晶致密化和显微结构的影响

doi: 10.11858/gywlxb.2001.03.011

周振君^1,3,,
李工^2,3,
杨正方¹,
陈玉如¹

1.
天津大学材料科学与工程学院，天津 300072；
2.
中国科学院物理研究所，北京 100080；
3.
燕山大学材料科学与化学工程学院，河北秦皇岛 066004

详细信息

通讯作者:
周振君

计量
- 文章访问数: 8072
- HTML全文浏览量: 482
- PDF下载量: 760
出版历程
- 收稿日期: 2001-01-16
- 修回日期: 2001-03-19
- 发布日期: 2001-09-05

The Effect of cBN Inclusions on the Densification and Microstructure of Fine-Grained Polycrystalline Diamond Compact

1.
The School of Materials Science and Engineering, Tianjin University, Tianjin 300072, China;
2.
Institute of Physics, Chinese Academy of Science, Beijing 100080;
3.
The College of Materials Science and Chemical Engineering, Yanshan University, Qinhuangdao 066004, China

More Information

Corresponding author: ZHOU Zhen-Jun

摘要

摘要: 以小于0.5 m的金刚石和氮化硼（以下简称cBN）微粉为原料，在6.0 GPa和1 450～1 480 ℃保温30 min的工艺条件下，成功地烧结出晶粒尺寸小于1 m、以WC/Co硬质合金为衬底的金刚石聚晶。研究了cBN掺杂对金刚石基质密实化和显微结构的影响。研究表明，cBN可以有效地抑制金刚石异常长大。细晶而且致密的金刚石聚晶有优异的力学性能。
- 金刚石烧结体 /
- 晶粒尺寸 /
- 立方氮化硼掺杂 /
- 致密化 /
- 显微结构
Abstract: Commercially available synthetic powders of diamond and cubic boron nitride less than 0.5 m were used as the raw materials. Sintering of a fine-grained polycrystalline diamond compact with grains less than 1 m in size was successfully carried out by making a laminate on a WC/Co powder compact under sintering conditions of 6.0 GPa and 1 450 ℃ to 1 480 ℃ for 30 min. The effect of cBN inclusions on the densification and microstructure of the polycrystalline diamond compact was investigated in detail. Results showed that cBN played the role of suppressing abnormal grain growth during sintering. The wear resistance of sintering diamonds with different volume fraction of cBN under sintering conditions of 6.0 GPa and 1 360 ℃ to1 480 ℃ for 30 min was measured. The microstructure of the polycrystalline diamond compact was observed by scanning electron microscope (SEM).
- sintering diamond /
- cBN inclusion /
- densification /
- microstructure /
- wear resistance

HTML全文

参考文献(7)

Wentorf R H, Devries R C, Bundy F P. Sintered Superhard Materials [J]. Science, 1980, 208: 873-880.

Gigl P D. High Pressure and Technology [M]. New York: Plenum Press, 1979: 914.

Hong S, Akaishi M, Kanda H, et al. Behavior of Cobalt Infiltration and Abnormal Grain Growth during Sintering of Diamond on Cobalt Substrate [J]. Journal of Materials Science, 1988, 23: 3831-3836.

Yazu, Hara A. Sintering Diamond Cutting Tools [P]. Japan Patent, 1986, No. 61-58432.

方啸虎. 合成金刚石的研究与应用 [M]. 北京: 地质出版社, 1996: 80-131.

Sudre O, Bao G, Fan B, et al. Effect of Inclusions on Densification: Numberical Model [J]. Journal of the American Ceramic Society, 1992, 75(3): 525-531.

Kingery W D. 陶瓷导论 [M]. 清华大学无机非金属材料教研组译. 北京: 中国建筑工业出版社, 1982: 451-520.

施引文献

资源附件(0)

访问统计