摘要: 用炸药爆轰的方法制备了纳米超微金刚石,对纳米超微金刚石进行了激光Raman光谱分析。研究发现,在1 321 cm-1和1 600 cm-1附近观察到了对应于sp3金刚石和sp2石墨的特征峰,金刚石的Raman峰向低波数方向移动了约10 cm-1,其半高宽约30 cm-1,同时在低波数方向出现尾巴,呈现非对称的Raman波谱。Raman光谱分析的结果与X射线衍射分析的结果符合。Abstract: Raman spectra of ultrafine diamond obtained from detonation are measured. The characteristic Raman bands assigned to sp3 diamond and sp2 graphite have been observed at around 1 321 cm-1 and 1 600 cm-1, respectively, in which the sp3 diamond band is asymmetric with the half-peak width of about 30 cm-1, with a tail towards lower Raman frequency and a shift of about -10 cm-1. The results obtained from Raman spectrum agree with that from X-ray diffraction.
-
Key words:
- detonation /
- ultrafine diamond /
- Raman spectroscopy
-
Campbell I H, Fauchet P M. Solid State Commun, 1986, 58: 739. Fauchet P M, Campbell I H. Crit Rev Solid State Mater Sci, 1988, 14: s79. Yoshikawa M, Mori Y, et al. Appl Phys Lett, 1993, 62(24): 14. Wada N, Solin S A. Physica B, 1981, 105: 353. 陈权. 炸药爆轰合成超微金刚石的理论及应用问题研究. 北京: 北京理工大学, 1998. 周刚. 利用炸药中的碳爆轰合成超细金刚石的研究. 北京: 北京理工大学, 1995. Ager J W, Veirs D K, et al. Phys Rev B, 1991, 43: 6491. Yoshikawa M, Mori Y, et al. Appl Phys Lett, 1995, 67(5): 31. Nemanich R J. Annu Rev Mater Sci, 1994, 9: 2839. 张立德, 牟季美. 纳米材料学. 沈阳: 辽宁科学技术出版社, 1994.
点击查看大图
计量
- 文章访问数: 7249
- HTML全文浏览量: 464
- PDF下载量: 545