Influence of Cr-Content on both Resistivity and Its Pressure Effect in Amorphous Fe-Zr Base Alloys
-
摘要: 在0.000 1~2.5 GPa范围不同静水压下,用四探针法详细测量了七种非晶态Fe90-xCrxZr10合金(x=2、4、7、10、13、16、20)的电阻率。结果表明:(1)常压室温电阻率0与FeZr基非晶合金中Cr含量成N形曲线关系;(2)当静水压增加时,七种非晶合金的约化电阻率(/0)都单调下降,x越大则电阻率下降的幅度越小;(3)非晶Fe90-xCrxZr10合金电阻率的压力系数对x的变化相当敏感;(4)为方便查值,给出了六种典型静水压下/0与x的曲线关系。最后,讨论了四种物理模型的选用以及相干交换散射在高压下的行为。Abstract: The resistivity of amorphous Fe90-xCrxZr10 (x=2, 4, 7, 10, 13, 16, 20) alloys was measured in detail by a 4-probe dc technique under different hydrostatic pressure from 0.000 1 GPa to 2.5 GPa. It is observed that: (1) The resistivity 0 at room temperature and atmosphere pressure varies in a manner similar to the alphabet N as the content of Cr in amorphous Fe-Zr base alloys increases; (2) Relative resistivity /0 of amorphous Fe90-xCrxZr10 alloy drops monotonously when the hydrostatic pressure increases, the more the content of Cr, the smaller the decrease of resistivity; (3) Pressure coefficient of amorphous Fe90-xCrxZr10 alloys is quite sensitive to the variation in x; (4) Relation between /0 and x under 6 typical pressure was given. Finally we discussed the seletion of four physical models and the behavior of coherent exchange scattering under high hydrostatic pressure.
-
Key words:
- amorphous alloy /
- Kondo-like effect /
- coherent exchange scattering
-
磨文山, 沈保根, 等. 物理学报, 1986, 35(5): 583. 沈保根, 主亦中, 等. 低温物理学报, 1990, 12(2): 113. 苏昉, 车荣钲, 等. 高压物理学报, 1990, 4(1): 63. Nagel S R. Phys Rev B, 1977, 16: 1694. Grest G S, Nagel S R. Phys Rev B, 1979, 19(7): 3571. Cochrane R W, et al. Phys Rev Lett, 1975, 35: 676. Korn D, et al. Phys Lett A, 1974, 47: 117. Asomoza R, et al. J Phys, F: Mat Phys, 1977, 7: 327. Gennes De, et al. J Phys Chem Solids, 1958, 4: 71. Asomoza R, et al. J Phys F, 1979, 9: 349. Fukamichi K, et al. J Appl Phys, 1982, 53: 2310. Dahlberg D, et al. J Appl Phys, 1984, 55(6): 1942. Bhatnagar A K, et al. J Non-Cryst Solids, 1984, 61-62: 1125.
点击查看大图
计量
- 文章访问数: 7735
- HTML全文浏览量: 318
- PDF下载量: 881