The Phase Diagram of Solid Solution 60%NaAlSi2O6-40%CaMgSi2O6 at High Temperatures and High Pressures
-
摘要: 在1.0~5.0 GPa、700~1 750 ℃条件范围内,对固溶体0.6NaAlSi2O6-0.4CaMgSi2O6进行了研究,探讨了该固溶体在高温高压下的存在行为,研究了由非晶态玻璃向翡翠转化过程中p-T作用的相图,得到的透辉石翡翠的晶胞参数为a=0.943 9 nm,b=0.857 3 nm,c=0.523 3 nm,=107.28和V=0.417 02 nm3。本实验中合成的宝石级翡翠为色泽温润,具有玻璃光泽,半透明的极富观赏性的透辉石翡翠。Abstract: The solid solution, 60%NaAlSi2O6-40%CaMgSi2O6 was studied under 1.0~5.0 GPa, 700~1 750 ℃ by using a cubic anvil press. A high-temperature and high-pressure phase diagram for this 60%NaAlSi2O6-40%CaMgSi2O6 solid solution was obtained. A translucent jewel (Jd0.6Di0.4) was obtained in our experiment, surface of which shines with a glorious green color. The unit cell parameters of synthetic Jd0.6Di0.4: a=0.953 9 nm, b=0.857 8 nm, c=0.523 3 nm, =107.28, and V=0.417 02 nm3.
-
Key words:
- diopside /
- jadeite /
- high pressure /
- high pressure /
- phase diagram
-
Bradt R C, et al. Am Mineral, 1973, 58: 727-732. 陈久华, 等. 无机材料学报, 1989, 4: 1-6. 南京大学. 结晶学与矿物学. 北京: 地质出版社, 1978: 444. Abs-Warbach, Neuhaus A. N Jb Miner Abh, 1976, 127: 213-241. Yoder H S Jr. Am J Sci, 1950, 248: 225-248, 312-334. Adams L H. Am J Sci, 1953, 251: 299-308. Yoder H S, Weir C E. Am J Sci, 1951, 249: 683-694. Robertson E C, et al. Am J Sci, 1957, 255: 115-137. 闫学伟, 等. 高等学校化学学报, 1986, 7: 569. 沈才唧, 等. 国外非金属矿与宝石, 1991, (2-3): 68-70. 叶大年, 金成伟. X射线粉末及其在岩石学中的应用. 北京: 科学出版社, 1984: 172-137. Maryellen Cameron, et al. Am Mineral, 1973, 58: 594-618. Prewitt C T, et al. Am Mineral, 1966, 51: 956-975. 彭文世, 刘高魁. 矿物红外光谱图集. 北京科学出版社, 1982: 351. Bell P M, Roseboom E H Jr. Min Soc Am, 1969, 2: 151-161.
点击查看大图
计量
- 文章访问数: 9263
- HTML全文浏览量: 2060
- PDF下载量: 766