Thermodynamic Analysis of Diamond Growth with Catalyst at HPHT

    Corresponding author: XU Bin
  • 摘要: 利用热力学中经典的G0判定法,探讨了Fe基触媒合成金刚石晶体生长中的碳源问题,在计算中考虑了各物相的体积随温度和压力的变化。结果表明:在金刚石形成之前,就有大量Fe3C形成,而在触媒法合成金刚石的温度和压力范围内,Fe3CC(金刚石)+3-Fe反应自由能和石墨金刚石相变自由能均为负值,但前者比后者的绝对值更大,这说明前者更容易发生。因此,从热力学角度看,Fe3C的形成降低了石墨转变为金刚石所要越过的势垒,使用Fe基触媒合成金刚石单晶的生长来源于Fe3C的分解而不是石墨的直接转化。同时推导出在1200 K以上石墨-金刚石的平衡p-T关系:peq(GPa)=1.036+0.00236T (K),与F.P.Bundy的平衡线非常接近,证明了本热力学计算方法的可行性。
  • [1] Gou Q Q. Structure Conversion Mechanism in Graphite-Diamond at HPHT [J]. Journal of Jilin University, 1974, (2): 52-63. (in Chinese)
    [2] 芶清泉. 高温高压下石墨变金刚石的结构转化机理 [J]. 吉林大学学报, 1974, (2): 52-63.
    [3] Zhang Z J, Li Z N, Chen J. Progress in Research of Growth Mechanism of Static Pressure Synthetic Diamond CGrystal [J]. Superhard Material Engineering, 2006, 18(3): 40-43. (in Chinese)
    [4] 张治军, 李正南, 陈坚. 静压法合成人造金刚石晶体生长机理的研究进展 [J]. 超硬材料工程, 2006, 18(3): 40-43.
    [5] Sung C. Mechanism of the Solvent-Assisted Graphite to Diamond Transition under High Pressure: Implications for the Selection of Catalyst [J]. High Temp High Press, 1995, 27: 41-46.
    [6] Pavel E, Baluta G, Barb D, et al. The Nature of the Metallic Inclusions in Synthetic Diamond Crystals Synthesized at 5. 5 GPa in Fe-C System [J]. Solid State Commun, 1990, 76: 531-533.
    [7] Sterenberg L E, Slesarev V N, Korsunskaya I A, et al. The Experimental Study of the Interaction between the Melt, Carbides, and Diamond in the Iron-Carbon System at High Pressure [J]. High Temp High Press, 1975, (7): 517-522.
    [8] Naka S, Tsuzuki A, Hirano S I. Diamond Formation and Behaviour of Carbides in Several 3d-Transition Metal-Graphite Systems [J]. J Mater Sci, 1984, 19: 259-262.
    [9] Solozhenko B L, Turkevich B Z. Kinetics of Diamond Crystallization from the Melt of the Fe-Ni-C System [J]. J Phys Chem B, 2002, 106(26): 6634-6637.
    [10] Xu B, Cui J J, Wang S H, et a1. Fine Structures of the Fe-Based Metal Film Covering Synthetic Diamond Single Crystal [J].Acta Materialia, 2005, 41(4): 444-448. (in Chinese)
    [11] 许斌, 崔建军, 王淑华, 等. 人造金刚石单晶铁基金属包膜的精细结构 [J]. 金属学报, 2005, 41(4): 444-448.
    [12] Xu B, Li M S, Gong J H, et a1. Mossbauer Parameters of the Fe-Based Metal Film Surrounding Diamond and Its Catalytic Effect during Diamond Synthesis [J]. Acta Materialia, 2004, 40(80): 810-814. (in Chinese)
    [13] 许斌, 李木森, 宫建红, 等. Fe基金属包膜的Mossbauer参量及其在金刚石合成中的催化作用 [J]. 金属学报, 2004, 40 (80): 810-814.
    [14] Xu B, Li M S, Yin L W, et a1. Investigation of Metallic Film Surrounding As-Grown Diamond form Fe-Ni-C System [J].Journal of the Chinese Ceramic Society, 2003, 31(5): 470-475. (in Chinese)
    [15] 许斌, 李木森, 尹龙卫, 等. 铁基触媒合成金刚石形成的金属包膜的组织结构 [J]. 硅酸盐学报, 2003, 31(5): 470-475.
    [16] Xu B, Li M S, Cui J J, et al. An Investigation of a Thin Metal Film Covering on HPHT As-Grown Diamond from Fe-Ni-C System [J]. Mater Sci Eng A, 2005, (396): 352-359.
    [17] Ye D L, Hu J H. Practical Data Hand Book of Inorganic Thermodynamics [M]. Beijing: Metalurgical Industry Press, 2002. (in Chinese)
    [18] 叶大伦, 胡建华. 实用无机物热力学数据手册 [M]. 北京: 冶金工业出版社, 2002.
    [19] Mounet N, Marzari N. High-Accuracy First-Principles Determination of the Structural, Vibrational and Thermodynamical Properties of Diamond, Graphite and Derivatives [J]. Phys Rev B, 2005, 71(20): 205214.
    [20] Morgan W C. Thermal Expansion Coefficients of Graphite Crystals [J]. Carbon, 1972, 10: 73-79.
    [21] Reeber R R, Wang K. Thermal Expansion, Molar Volume and Specific Heat of Diamond from 0 to 3000 K [J]. J Elect Mater, 1996, 25(1): 63-67.
    [22] Bundy F P, Bovenkerk H P, Strong H M, et al. Diamond-Graphite Equilibrium Line from Growth and Graphitization of Diamond [J]. J Chem Phys, 1961, 35(2): 383-391.
    [23] Bundy F P, Bassett W A, Weathers M S, et al. The Pressure-Temperature Phase and Transformation Diagram for Carbon; Updated through 1994 [J]. Carbon, 1996, 34(2): 141-153.
    [24] The Chinese Society for Metals, The Nonferrous Metals Society of China. Physical Performances and Measuring Methods of Metals [M]. Beijing: MetalurgicalIndustry Press, 1987: 249. (in Chinese)
    [25] 中国金属学会, 中国有色金属学会. 金属物理性能及测试方法 [M]. 北京: 冶金工业出版社, 1987: 249.
    [26] Michal M, Paul E, Karsten A. Analytic Bond-Order Potential for bcc and fcc Iron-Comparison with Established Embedded-Atom Method Potentials [J]. J Phys: Condens Matter, 2007, 19: 326220.
    [27] Wood I G, Lidunka V, Knight K S, et al. Thermal Expansion and Crystal Structure of Cementite, Fe3C, between 4 and 600 K Determined by Time-of-Flight Neutron Powder Diffraction [J]. J Appl Crys, 2004, 37: 82-90.
    [28] Scott H P, Williams Q, Knittle E. Stability and Equation of State of Fe3C to 73 GPa: Implications of Carbon in the Earth's Core [J]. Geop Res Lett, 2001, 28(9): 1875-1878.
  • [1] 李丽许斌宫建红李木森 . 高温高压合成金刚石中触媒的价电子结构分析. 高压物理学报, 2006, 20(4): 372-378 . doi: 10.11858/gywlxb.2006.04.006
    [2] 肖万生翁克难律广才汪本善 . 聚乙烯与水反应的高温高压实验及热力学探讨. 高压物理学报, 2001, 15(3): 169-177 . doi: 10.11858/gywlxb.2001.03.002
    [3] 丁立业罗湘捷若规雅男乡郎田靖李伟 . 金刚石生长的高压溶剂中碳的输运及其影响. 高压物理学报, 1994, 8(2): 146-152 . doi: 10.11858/gywlxb.1994.02.009
    [4] 马贤锋阎学伟倪嘉缵崔硕景苏文辉千正男王一锋 . 高压合成立方氮化硼用的新触媒材料的研究. 高压物理学报, 1988, 2(3): 264-269 . doi: 10.11858/gywlxb.1988.03.010
    [5] 亓曾笃 . 人造金刚石生长中的温度控制. 高压物理学报, 1990, 4(3): 204-209 . doi: 10.11858/gywlxb.1990.03.006
    [6] 李良彬江锦春杨信道钟毓茂张欣苑洪时明 . 碳化钒作碳源合成金刚石. 高压物理学报, 1998, 12(2): 141-144 . doi: 10.11858/gywlxb.1998.02.012
    [7] 张铁臣马文骏郭伟力徐晓伟邹广田 . Ca3B2N4-hBN系中立方氮化硼的膜生长机制. 高压物理学报, 1992, 6(4): 273-278 . doi: 10.11858/gywlxb.1992.04.005
    [8] 刘磊张元培王风陈冲李木森 . 高温高压下金刚石单晶生长过程的声发射动态特征. 高压物理学报, 2010, 24(6): 409-414 . doi: 10.11858/gywlxb.2010.06.002
    [9] 唐功本石风孙万明崔硕景师昌怀谢云芬王增林倪加缵 . 预处理石墨对合成金刚石性能的影响. 高压物理学报, 1990, 4(4): 300-304 . doi: 10.11858/gywlxb.1990.04.010
    [10] 苏作鹏张铁臣杜勇慧 . 高压高温下B2O3与Mg和Li3N的反应. 高压物理学报, 2006, 20(3): 277-280 . doi: 10.11858/gywlxb.2006.03.009
    [11] 郝兆印高春晓罗薇邹广田程开甲程漱玉 . 高温高压金刚石单晶生长界面的研究. 高压物理学报, 1997, 11(3): 169-174 . doi: 10.11858/gywlxb.1997.03.002
    [12] 刘万强马洪安贾晓鹏 . FeMn粉末触媒对合成金刚石的影响. 高压物理学报, 2011, 25(6): 572-576. doi: 10.11858/gywlxb.2011.06.014
    [13] 李和胜李木森 . 高温高压下Fe-Ni-C系合成金刚石的研究. 高压物理学报, 2007, 21(4): 401-408 . doi: 10.11858/gywlxb.2007.04.012
    [14] 卢景瑞寇自力刘腾张雷雷丁未张强王强杨鸣龚红霞贺端威 . 亚微米级聚晶金刚石的高温高压合成. 高压物理学报, 2018, 32(2): 023302-1-023302-7. doi: 10.11858/gywlxb.20170574
    [15] 罗湘捷丁立业刘强叶俐罗伯诚 . 高温高压下B4C合成金刚石的研究. 高压物理学报, 1997, 11(4): 266-269 . doi: 10.11858/gywlxb.1997.04.006
    [16] 王遥马红安杨志强丁路遥王战轲贾晓鹏 . 籽晶{100}面形状对高温高压合成金刚石大单晶的影响. 高压物理学报, 2019, 33(4): 043301-1-043301-7. doi: 10.11858/gywlxb.20190708
    [17] 郝兆印贺义兴陈宇飞王德荣王琰弟 . 高温高压条件下石墨的再结晶与金刚石单晶的生长. 高压物理学报, 1992, 6(2): 81-91 . doi: 10.11858/gywlxb.1992.02.001
    [18] 吴奇孙力玲景勤曹新成王文魁 . 超临界流体触媒作用下石墨-金刚石转变. 高压物理学报, 2002, 16(1): 1-6 . doi: 10.11858/gywlxb.2002.01.001
    [19] 徐晓伟邹广田张铁臣郭伟力马文骏郭学斌 . Mg3N2和Mg3B2N4触媒的研究. 高压物理学报, 1992, 6(4): 279-284 . doi: 10.11858/gywlxb.1992.04.006
    [20] 韩晶晶贺端威马迎功丁未芶立唐永建 . 类金刚石微球的高温高压制备. 高压物理学报, 2017, 31(3): 215-222. doi: 10.11858/gywlxb.2017.03.002
  • 加载中
计量
  • 文章访问数:  4079
  • 阅读全文浏览量:  149
  • PDF下载量:  901
出版历程
  • 收稿日期:  2008-08-11
  • 录用日期:  2009-01-20
  • 刊出日期:  2009-06-15

高温高压触媒法金刚石生长的热力学分析

    通讯作者: 许斌; 
  • 1. 山东建筑大学材料科学与工程学院,山东济南 250101;
  • 2. 河北工程大学机电学院,河北邯郸 056038;
  • 3. 山东大学材料科学与工程学院,山东济南 250061

摘要: 利用热力学中经典的G0判定法,探讨了Fe基触媒合成金刚石晶体生长中的碳源问题,在计算中考虑了各物相的体积随温度和压力的变化。结果表明:在金刚石形成之前,就有大量Fe3C形成,而在触媒法合成金刚石的温度和压力范围内,Fe3CC(金刚石)+3-Fe反应自由能和石墨金刚石相变自由能均为负值,但前者比后者的绝对值更大,这说明前者更容易发生。因此,从热力学角度看,Fe3C的形成降低了石墨转变为金刚石所要越过的势垒,使用Fe基触媒合成金刚石单晶的生长来源于Fe3C的分解而不是石墨的直接转化。同时推导出在1200 K以上石墨-金刚石的平衡p-T关系:peq(GPa)=1.036+0.00236T (K),与F.P.Bundy的平衡线非常接近,证明了本热力学计算方法的可行性。

English Abstract

参考文献 (28)

目录

    /

    返回文章
    返回