Failure Modes of Ductile Metal Plates under Normal Impact by Flat-Ended Projectiles
-
摘要: 对延性金属靶板在刚性平头弹丸正撞击下的破坏模式进行了研究。一般而言,延性金属靶板的破坏模式可以分为两种:带有总体变形的局部简单剪切破坏和局部化的绝热剪切冲塞破坏。首先基于Bai-Johnson热塑性本构关系建立了一个局部化的绝热剪切冲塞模型,然后结合描述带有总体变形的局部简单剪切破坏的Wen-Jones模型,找出了两种模型之间转化的临界条件。理论预测与文献中的实验结果吻合得很好。Abstract: This paper examines the failure modes of ductile metal plates subjected to impact by rigid flat-ended projectiles at normal incidence. General speaking, there are two failure modes which can occur in a ductile metal plate: simple shear failure with global deformation, and localized adiabatic shear plugging. Based on the thermoplastic constitutive relationship of Bai and Johnson, an adiabatic shear plugging model is first proposed. When combined with the Wen-Jones model which describes simple shear failure with global response, a critical condition for the change in these two failure modes is obtained. It transpires that the present theoretical predictions are in good agreement with available experimental observations in terms of failure modes and ballistic limits.
-
Woodward R L, Morton M E DE. Penetration of Targets by Flat-Ended Projectiles [J]. Int J Mech Sci, 1976, 18: 119-127. Woodward R L. The Interrelation of Failure Modes Observed in the Penetration of Metallic Targets [J]. Int J Impact Eng, 1984, 2(2): 121-129. Woodward R L. A Structural Model for Thin Plate Perforation by Normal Impact of Blunt Projectiles [J]. Int J Impact Eng, 1987, 6: 4129-140. Woodward R L, Cimpoeru S J. A Study of the Perforation of Aluminium Laminate Targers [J]. Int J Impact Eng, 1998, 21(3): 117-131. Bai Y L, Johnson W. Plugging: Physical Understanding and Energy Absorption [J]. Metals Technol, 1982, 9: 182-190. Langseth M, Larsen P K. Dropped Objects' Plugging Capacity of Steel Plates: an Experimental Investigation [J]. Int J Impact Eng, 1990, 9(3): 289-316. Langseth M, Larsen P K. The Behaviour of Square Steel Plates Subjected to a Circular Blunt Ended Load [J]. Int J Impact Eng, 1992, 12(4): 617-638. Langseth M, Larsen P K. Dropped Objects' Plugging Capacity of Aluminium Alloy Plates [J]. Int J Impact Eng, 1994, 15(3): 225-241. Wen H M, Jones N. Semi-Empirical Equations for the Perforation of Plates Struck by a Mass [A]//Structure under Shock and Impact (SUSI)Ⅱ, Computational Mechanics Publications, 1992: 369-380. Wen H M, Jones N. Low-velocity Perforation of Punch-Impact-Loaded Metal Plates [J]. Pressure Vessel Technol, 1996, 118(2): 181-187. Wen H M, Jones N. Experimental Investigation into the Dynamic Plastic Response and Perforation of a Clamped Circular Plate Struck Transversely by a Mass [A]//Proceedings of the Institution of Mechanical Engineers, J Mech Eng Sci, 1994, 208(C2): 113-37. Wen H M, Jones N. Experimental Investigation of the Scaling Laws for Metal Plates Struck by Large Mass [J]. Int J Impact Eng, 1993, 13(3): 485-505. Corran R S J, Shadbolt P J, Ruiz C. Impact Loading of Plates-an Experimental Investigation [J]. Int J Impact Eng, 1983, 1(1): 3-22. Corbet G Gt, Reid S R. Quasi-Static and Dynamic Local Loading of Monolithic Simply-Supported Steel Plate [J]. Int J Impact Eng, 1993, 13(3): 423-441. Borvik T, Langseth M, Hopperstad O S, et al. Ballistic Penetration of Steel Plates. Int J Impact Eng, 1999, 22: 855-886. Borvik T, Hopperstad O S, Berstad T, et al. Numerical Simulation of Plugging Failure in Ballistic Penetration [J]. Int J Solids Struct, 2001, 38: 6241-6264. Borvik T, Leinum J R, Solberg J K, et al. Observations on Shear Plug Formation in Weldox 460 E Steel Plates Impacted by Blunt-Nosed Projectiles [J]. Int J Impact Eng, 2001, 25: 553-572. Borvik T, Langseth M, Hopperstad O S, et al. Perforation of 12 mm Thick Steel Plates by 20 mm Diameter Projectiles with Flat, Hemispherical and Conical Noses Part I: Experimental Study [J]. Int J Impact Eng, 2002, 27: 19-35. Borvik T, Hopperstad O S, Langseth M, et al. Effect of Target Thickness in Blunt Projectile Penetration of Weldox 460 E Steel Plates [J]. Int J Impact Eng, 2003, 28: 413-464. Chen X W, Li Q M, Fan S C. Initiantion of Adiabatic Shear Failure in a Clamped Circular Plate Struck by a Blunt Projectile [J]. Int J Impact Eng, 2005, 31: 877-893. Kalthoff J F, Winkler S. Failure Mode Transition of High Rates of Shear Loading [A]//Chiem CY, Kunze H-D, Meyer LW. Proceedings of the Intermational Conference on Impact Loading and Dynamics Behavior of Materials [C]. Germany: Deutsche Gesellschaft fr Metallkunde, DGM-Verlag, Oberursel, 1988: 185-195. Kalthoff J F, Winkler S. Transition in the Failure Behaviour of Dynamically Shear Loaded Cracks [J]. Appl Mech Rev, 1990, 43(5): 250-287. Kalthoff J F, Brgel A. Influence of Loading Rate on Shear Fracture Toughness for Failure Mode Transition [J]. Int J Impact Eng, 2004, 30: 957-971. Dong X L, Wang L L, Yu J L. An Investigation on Shear Fracture under Impact Loading [J]. Journal of Ningbo University(nsee), 2003, 16: 429-433. Mu J C. Study on Typical Rupture Modes of Thin Metal Plates under Normal Impact by Conical-Nosed Missiles [J]. Explosion and Shock Waves, 2005, 25: 74-79. (in Chinese) 穆建春. 金属薄板在圆锥头弹体正冲击下的破裂模式 [J]. 爆炸与冲击, 2005, 25: 74-79. Wen H M, Rao W F. Deformation and Perforation of Simply Supported Circular Plates Struck Normally by Flat-Faced Projectiles [J]. Chinese Journal of High Pressure Physics, 2005, 19(1): 51-58. Teng X, Wierzbicki T. Dynamic Shear Plugging of Beams and Plates with an Advancing Crack [J]. Int J Impact Eng, 2005, 31: 667-698.
点击查看大图
计量
- 文章访问数: 14331
- HTML全文浏览量: 872
- PDF下载量: 1082