Shock-Induced Phase Transition and Spallation in Pure Iron under Magnetically Driven Flyer Plate Loading
-
摘要: 使用磁驱动装置CQ-4发射紫铜飞片对纯铁样品进行一维平面应变加载,采用高精度激光位移干涉仪(DPS)记录飞片和样品的自由面速度历史。结果显示,当纯铁样品在加、卸载过程中有α ↔ε相变发生时,样品的层裂强度达到3.4 GPa,比已报道的未发生相变的纯铁的层裂强度(1.2~1.9 GPa)有明显提高,其原因可能是纯铁材料在经历α ↔ε可逆相变时,内部晶格产生了大量的位错。通过分析样品的自由面速度历史,判断出样品发生了自由面浅表层裂现象。在对飞片和样品中的应力波系进行分析时,若只考虑塑性波和相变波在界面的反射稀疏波与飞片传入样品靶中的稀疏波之间的相互作用,将无法解释实验观测到的自由面浅表层裂现象,因此该现象可能与纯铁样品在逆相变过程中产生稀疏冲击波有关。Abstract: The magnetically driven device CQ-4 was used to drive a copper flyer plate to impact a pure iron specimen to achieve one dimensional plane-wave loading, and a high-accurate Doppler pin system was utilized to record the free-surface velocity histories of the flyer and specimen.The results indicate that if the pure iron material experiences α ↔ε phase transition during shock loading and unloading, its spallation strength reaches to 3.4 GPa which is distinctly higher than the reported value of 1.2-1.9 GPa without phase transition.The possible cause of this phenomenon is that a multitude of dislocations in the crystal lattices of the pure iron are formed during the α ↔ε reversible phase transition.Moreover, the free-surface velocity history reveals that the spallation has occurred in the near-surface of the specimen.The formation of the shallow spallation may be related to the rarefaction wave formed at the time of reversal phase transition in the pure iron specimen.Because if only consider the interactions between the rarefaction waves generated by the reflection of plastic wave as well as phase transition wave and rarefaction wave when analyzing the stress wave propagations in the flyer-specimen system, it is impossible to interpret the detected shallow spallation in the experiment.
-
表 1 实验参数
Table 1. Experimental parameters
Exp.No. Flyer size/
(mm×mm×mm)Specimen size/
(mm×mm)dAl/(μm) U/(kV) v /(m/s) pmax/(GPa) Remarks 1 23×12×1.3 75 1 594 Testing for planarity and velocity 2 23×12×1.3 65 1 325 Testing for planarity and velocity 3 23×12×1.3 Ø8.0×0.8 1.5 65 1 302 28.1 Loading on the Fe specimen 表 2 样品和飞片的材料参数
Table 2. Material parameters of the specimen and flyer
Material Density/(g/cm3) Hugoniot parameters Longitude sound velocity/(km/s) c0/(km/s) λ Fe (Specimen) 7.85 4.63 1.33 5.97 Cu (Flyer) 8.93 3.94 1.49 4.76 -
[1] Bancroft D, Peterson E L, Minshall S. Polymorphism of iron at high pressure[J]. J Appl Phys, 1956, 27(3): 291-298. doi: 10.1063/1.1722359 [2] Christophe V, Francois B, Gilles R. Study of spalling for high purity iron below and above induced α↔β phase transition[C]//Furnish M D, Cupta Y M, Forbes J M. Shock Compression of Condensed Matter-2003. New York: American Institute of Physics, 2004: 511-514. [3] Gray G T, Hayes D B, Hixson R S. Influence of the shock-induced α-ε transition in Fe on its post-shock substructure evolution and mechanical behavior[J]. J Phys Ⅳ France, 2000, 10(9): 755-760. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=6faec4dad1534ed54208dfa204f3a00a [4] Veeser L R, Gray G T, Vorthman J E, et al. High pressure response of a high-purity iron[C]//Furnish M D, Chhabidas L C, Hixson R S. Shock Compression of Condensed Matter-1999. Snowbird, Utah: American Institute of Physics, 2000: 73-76. [5] 陈永涛, 唐小军, 李庆忠, 等.纯铁材料的冲击相变与"反常"层裂[J].爆炸与冲击, 2009, 29(6): 637-641. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=bzycj200906014Chen Y T, Tang X J, Li Q Z, et al. Phase transition and abnormal spallation in pure iron[J]. Explosion and Shock Waves, 2009, 29(6): 637-641. (in Chinese) http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=bzycj200906014 [6] 陈永涛, 李庆忠, 唐小军, 等.给定压力下纯铁材料的冲击相变与层裂特性研究[J].高压物理学报, 2010, 24(3): 213-218. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=gywlxb201003009Chen Y T, Li Q Z, Tang X J, et al. Study on phase transition and spallation of pure iron under given pressure[J]. Chinese Journal of High Pressure Physics, 2010, 24(3): 213-218. (in Chinese) http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=gywlxb201003009 [7] 孙承纬, 赵剑衡, 王桂吉, 等.磁驱动准等熵平面压缩和超高速飞片发射实验技术原理、装置及应用[J].力学进展, 2012, 42(2): 206-219. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=lxjz201202008Sun C W, Zhao J H, Wang G J, et al. Progress in magnetic loading techniques for isentropic compression experiments and ultra-high velocity flyer launching[J]. Advances in Mechanics, 2012, 42(2): 206-219. (in Chinese) http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=lxjz201202008 [8] Wang G J, Luo B Q, Zhang X P, et al. A 4 MA, 500 ns pulsed power generator CQ-4 for characterization of material behaviors under ramp wave loading[J]. Rev Sci Instrum, 2013, 84(1): 015117. doi: 10.1063/1.4788935 [9] 李雪梅, 俞宇颖, 张林, 等. 〈100〉LiF的低压冲击响应和1 550 nm波长下的窗口速度修正[J].物理学报, 2012, 61(15): 156202. http://www.cnki.com.cn/Article/CJFDTotal-WLXB201215062.htmLi X M, Yu Y Y, Zhang L, et al. Elastic-plastic response of shocked 〈100〉 LiF and its window correction at 1 550 nm wavelength[J]. Acta Physica Sinica, 2012, 61(15): 156202. (in Chinese) http://www.cnki.com.cn/Article/CJFDTotal-WLXB201215062.htm [10] 陈永涛, 唐小军, 李庆忠. Fe基α相合金的冲击相变及其对层裂行为的影响研究[J].物理学报, 2011, 60(4): 046401. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=wlxb201104079Chen Y T, Tang X J, Li Q Z. Phase transition and influence of phase transitionon spall in α phase Fe-based alloy[J]. Acta Physica Sinica, 2011, 60(4): 046401. (in Chinese) http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=wlxb201104079 [11] 唐小军, 胡海波, 李庆忠, 等. HR2钢及几种铁基材料的冲击相变行为[J].爆炸与冲击, 2006, 26(2): 115-120. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=bzycj200602003Tang X J, Hu H B, Li Q Z, et al. Experimental studies on shock-induced phase transition in HR2 and other Fe-based materials[J]. Explosion and Shock Waves, 2006, 26(2): 115-120. (in Chinese) http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=bzycj200602003 [12] 张兴华, 唐志平, 徐薇薇, 等. FeMnNi合金的冲击相变和层裂特性的实验研究[J].爆炸与冲击, 2007, 27(2): 103-108. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=bzycj200702002Zhang X H, Tang Z P, Xu W W, et al. Experimental study on characteristics of shock-induced phase transition and spallation in FeMnNi alloy[J]. Explosion and Shock Waves, 2007, 27(2): 103-108. (in Chinese) http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=bzycj200702002